　WANG Dong,ZHENG Yi,LI Lin,et al. Low-temperature properties of Buton rock-modified asphalt with different particle sizes [J].Journal of Wuhan Institute of Technology,2026,48(02):231-236.[doi:10.19843/j.cnki.CN42-1779/TQ.202209015]
点击复制

不同粒径布敦岩改性沥青的低温性能研究
(/HTML)

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
48
期数:
2026年02期
页码:
231-236
栏目:
智能制造
出版日期:
2026-04-30

文章信息/Info

Title:
Low-temperature properties of Buton rock-modified asphalt with different particle sizes
文章编号:
1674 - 2869（2026）02 - 0231 - 06
作者:
王 栋1; 郑 益2; 李 琳1; 胡小弟1; 潘 攀*1
1.武汉工程大学土木工程与建筑学院，绿色土木工程材料与结构湖北省工程研究中心, 湖北 武汉 430074；2.武汉汇科质量检测有限责任公司，湖北 武汉 430050
Author(s):
WANG Dong1;  ZHENG Yi2;  LI Lin1;  HU Xiaodi1;  PAN Pan*1
1. School of Civil Engineering and Architecture, Wuhan Institute of Technology, Hubei Provincial Engineering Research Center for Green Civil Engineering Materials and Structures， Wuhan 430074, China;
2. Wuhan Huike Quality Testing Co., Ltd, Wuhan 430050, China

关键词:
道路工程; 布敦岩沥青; 灰分; 沥青混合料; 低温性能
Keywords:
road engineering;  Buton rock asphalt;  ash;  asphalt mixture;  low-temperature property
分类号:
U414
DOI:
10.19843/j.cnki.CN42-1779/TQ.202209015
文献标志码:
A
摘要:
为了研究不同粒径布敦岩沥青(BRA)和BRA灰分对改性沥青低温性能的影响，以5种不同粒径的BRA及BRA灰分作为研究对象，通过沥青物理性能试验、流变性能试验、四组分试验，以及沥青混合料低温弯曲小梁试验、半圆弯曲试验对比研究了不同粒径的BRA对沥青及沥青混合料低温性能的影响规律。结果表明：BRA和BRA灰分的粒径越大，改性沥青胶浆及沥青混合料的低温性能越差。当粒径相同时，BRA改性沥青中沥青质含量高于BRA灰分改性胶浆，且前者低温性能较后者更差。兼顾其低温性能和经济性，推荐BRA的最佳粒径为16.8 μm。
Abstract:
The effects of Buton rock asphalt (BRA) and BRA ash of five different particle sizes on the low-temperature properties of asphalt and asphalt mixture were studied by the physical property test, rheological property test, four constituent chemical test, low-temperature bending test and semi-circular bending test. The findings indicated that increasing the particle sizes of BRA and BRA ash contributes to the degradation of the low-temperature properties of the modified asphalts. When the particle size of BRA is the same, the asphalt content of BRA-modified asphalt binder is more than that of the BRA ash-modified asphalt mortar, and the BRA-modified asphalt binder shows worse low-temperature properties than the BRA-modified asphalt mortar. Thus, we recommend to use the BRA with a size of 16.8 μm to prepare the BRA-modified asphalt in consideration of low-temperature properties and economy.

参考文献/References:

[ 1 ] 李亚非, 闫瑾, 陈景. 活化“湿法” 加工布敦岩沥青及沥青混合料路用性能研究[J]. 中外公路, 2020, 40(3): 308-311.
[ 2 ] 贾睿. 灌注式岩沥青混合料力学性能及施工技术研究[J]. 福建交通科技, 2020(2): 28-30.
[ 3 ] HADIWARDOYO S P, SINAGA E S, FIKRI H. The influence of Buton asphalt additive on skid resistance based on penetration index and temperature [J]. Construction and Building Materials, 2013, 42: 5-10.
[ 4 ] KARAMI M. Assessing the fatigue performance of Buton rock asphalt modified mixtures [J]. International Journal of Pavement Research and Technology, 2020, 13(5): 536-547.
[ 5 ] KARAMI M, NIKRAZ H, SEBAYANG S, et al. Laboratory experiment on resilient modulus of BRA modified asphalt mixtures [J]. International Journal of Pavement Research and Technology, 2018, 11(1): 38-46.
[ 6 ] MIRZAIYAN D, AMERI M, AMINI A, et al. Evaluation of the performance and temperature susceptibility of Gilsonite- and SBS-modified asphalt binders [J]. Construction and Building Materials, 2019, 207: 679-692.
[ 7 ] YAN K Z, ZHANG M, YOU L Y, et al. Performance and optimization of castor beans-based bio-asphalt and European rock-asphalt modified asphalt binder [J]. Construction and Building Materials, 2020, 240: 117951.
[ 8 ] 张思桐, 吕秀明, 肖利明. 废胎胶粉目数和加工时间对橡胶沥青性能的影响[J]. 公路交通科技(应用技术版), 2016, 12(10): 124-125.
[ 9 ] 涂娟, 袁军, 包传平, 等. 废橡胶粉对SBS改性沥青的老化性能影响研究[J]. 武汉工程大学学报, 2009, 31(3): 19-22.
[10] 杨勇, 黄鹏, 周文, 等. 高灰分岩沥青改性沥青混合料路用性能及其作用机理研究[J]. 公路交通科技(应用技术版), 2019, 15(5): 22-25.
[11] 中华人民共和国交通运输部. 公路工程沥青及沥青混合料试验规程: JTG E20—2011[S]. 北京: 人民交通出版社, 2011.
[12] 中华人民共和国交通运输部. 公路工程集料试验规程: JTG E42—2005[S]. 北京: 人民交通出版社, 2005.
[13] 朱桃. 布敦岩沥青(BRA)改性沥青结合料使用性能研究[D]. 长沙: 湖南大学, 2014.
[14] 李瑞霞. BRA岩沥青及其混合料技术特性研究[D]. 西安: 长安大学, 2010.
[15] 叶茂, 胡小弟, 孙权, 等. 硫磺改性沥青混合料基本性能的研究[J]. 武汉工程大学学报, 2017, 39(4): 366-371.

相似文献/References:

[1]沈凡,钟亚聃,向天翔,等.再生剂在再生沥青混合料中的扩散融合行为研究 [J].武汉工程大学学报,2025,47(06):629.[doi:10.19843/j.cnki.CN42-1779/TQ.202411004]
　SHEN Fan,ZHONG Yadan,XIANG Tianxiang,et al. Diffusion and fusion behavior of rejuvenator in recycled asphalt mixture [J].Journal of Wuhan Institute of Technology,2025,47(02):629.[doi:10.19843/j.cnki.CN42-1779/TQ.202411004]

备注/Memo

备注/Memo:
收稿日期：2022-09-13
基金项目：湖北省自然科学基金(2019CF330)；湖北省交通运输厅科技项目（2022-11-1-2）
作者简介：王 栋，硕士研究生。Email: 954867892@qq.com
*通信作者：潘 攀，博士，副教授。Email: panpan8597@126.com
更新日期/Last Update: 2026-05-07