|本期目录/Table of Contents|

[1]陈　杰,罗　喆,苏勇杰,等.有机胺共沉淀法制备镍钴铝三元前驱体及表征[J].武汉工程大学学报,2019,(05):457-460.[doi:10. 3969/j. issn. 1674?2869. 2019. 05. 009]
　CHEN Jie,LUO Zhe,SU Yongjie,et al.Preparation and Characterization of Nickel-Cobalt-Aluminum Ternary Precursors by Organic Amine Co-Precipitation[J].Journal of Wuhan Institute of Technology,2019,(05):457-460.[doi:10. 3969/j. issn. 1674?2869. 2019. 05. 009]
点击复制

有机胺共沉淀法制备镍钴铝三元前驱体及表征(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
期数:
2019年05期
页码:
457-460
栏目:
材料科学与工程
出版日期:
2021-01-24

文章信息/Info

Title:
Preparation and Characterization of Nickel-Cobalt-Aluminum Ternary Precursors by Organic Amine Co-Precipitation
文章编号:
20190509
作者:
陈　杰; 罗　喆; 苏勇杰; 张　勇*; 吴江渝
武汉工程大学材料科学与工程学院，湖北 武汉 430205
Author(s):
CHEN Jie; LUO Zhe; SU Yongjie; ZHANG Yong*; WU Jiangyu
School of Materials Science and Engineering，Wuhan Institute of Technology，Wuhan 430205， China
关键词:
镍钴铝; 三元前驱体; 二正丁胺; 共沉淀
Keywords:
nickel-cobalt-aluminum ;  ternary precursors;  di-n-butylamine;  co-precipitation
分类号:
TQ126.3+5
DOI:
10. 3969/j. issn. 1674?2869. 2019. 05. 009
文献标志码:
A
摘要:
以硝酸镍、硝酸钴、硝酸铝和二正丁胺为原料，通过有机胺共沉淀法制备了镍钴铝（NCA）三元前驱体Ni0.8Co0.15Al0.05（OH）2，并利用X衍射分析仪、扫描电子显微镜、粒度分析仪和热重分析仪对其晶体结构、形貌和化学组成进行表征。在室温条件下向硝酸盐溶液中加入二正丁胺，反应后将溶液过滤，并将得到的固体进行洗涤和干燥，以获得可用于锂电池正极材料镍钴铝酸锂生产的NCA三元前驱体Ni0.8Co0.15Al0.05（OH）2。实验结果表明最佳的反应条件为硝酸盐溶液浓度1 mol/L，搅拌速率400 r/min，反应温度80 ℃，所得NCA三元前驱体为组分均匀的类球型颗粒，粒度分布在14.666~40.094 μm之间。本文提出Ni0.8Co0.15Al0.05（OH）2的生产制备方法大量减少了工业废水的产生，降低了工业生产成本。
Abstract:
The nickel-cobalt-aluminum （NCA） ternary precursors Ni0.8Co0.15Al0.05（OH）2 were prepared by organic amine co-precipitation method with ferric nitrate，cobalt nitrate，aluminium nitrate and dibutylamine as the precursors. The crystal structure，morphology and chemical component of the products were characterized by X-ray diffractometry，scanning electron microscopy，particle size analyzer and thermal gravimetric analyzer. Di-n-butylamine was added to the nitrate solution at room temperature. After the reaction， the solution was filtered. The obtained solid was washed and dried to obtain NCA ternary precursor Ni0.8Co0.15Al0.05（OH）2 which can be used for lithium battery cathode material LiNi0.8Co0.05Al0.15O2 production. The results show that the obtained NCA ternary precursor is a homogeneous sphere-like particle with the size of 14.666-40.094 μm at nitrate solution concentration of 1 mol/L， stirring rate of 400 r/min，and reaction temperature of 80 ℃. The production method of Ni0.8Co0.15Al0.05（OH）2 greatly reduces the prodution of industrial wastewater and the cost of industrial production.

参考文献/References:

［1］　张卜升，吴永谦，张科，等.镍钴铝三元正极材料研究进展［J］.广州化工，2017，45（11）：3-5.［2］　叶超. 锂离子电池镍钴铝三元正极材料的制备及性能研究［D］.广州：华南理工大学，2017.［3］　CHO Y， CHO J. Significant improvement of LiNi0.8Co0.15Al0.05O2 cathodes at 60 ℃ by SiO2 dry coating for Li-ion batteries［J］. Journal of the Electrochemical Society，2010，157（6）：625-629. ［4］　KIM Y， CHO J. Lithium-reactive Co3（PO4）2 nanoparticle coating on high-capacity LiNi0.8Co0.16Al0.04O2 cathode material for lithium rechargeable batteries［J］. Journal of the Electrochemical Society，2007，154（6）：495-499. ［5］　李军，刘建军，李少芳，等. 锂离子电池三元正极材料镍钴铝酸锂的研究进展［J］. 化工新型材料，2016，44（6）：49-51. ［6］　齐然. 锂离子电池高比容量NCA正极材料研究［D］. 天津：天津工业大学，2017. ［7］　余剑琳. 锂离子电池三元正极材料NCA的制备及改性研究［D］. 广州：广东工业大学，2018. ［8］　阮泽文. LiNi（1-x-y）CoxAlyO2高镍三元正极材料的制备及改性研究［D］. 哈尔滨：哈尔滨工业大学，2016. ［9］　张正国，欧昌洪，康慧芬，等. 共沉淀法制备锂电池三元正极材料浅析［J］. 化工管理，2012（增刊1）：33-34. ［10］　王明志. 锂离子电池正极材料LiNi0.8Co0.15Al0.05O2的制备及性能研究［D］. 大连：大连海事大学，2017. ［11］　邱振平，张英杰，董鹏，等. LiNi0.8Co0.15Al0.05O2正极活性材料的衰减机理及改性措施［J］. 材料导报，2017，31（1）：18-24. ［12］　LI X，XIE Z W，LIU W J，et al. Effects of fluorine doping on structure，surface chemistry，and electrochemical performance of LiNi0.8Co0.15Al0.05O2［J］. Electrochimica Acta，2015，174：1122-1130. ［13］　徐晟. 锂离子电池富镍三元材料的合成放大化和改性研究［D］. 哈尔滨：哈尔滨工业大学，2017. ［14］　刘秀庆，向波，曲冬雪，等. 三元材料前驱体生产中氨氮废水产生机理及治理技术［J］. 世界有色金属，2017（8）：4-8. ［15］　李健昌，封丹，罗仙平，等. 氨氮工业废水处理技术现状和展望［J］. 四川有色金属，2008（3）：41-44，35. ［16］　任义，王磊，狄雅茹. 氨氮废水处理技术进展综述［J］. 西安文理学院学报（自然科学版），2008（3）：90-93.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期：2018-10-11作者简介：陈　杰，硕士研究生。E-mail：794612979@qq.com*通讯作者：张　勇，博士，教授。E-mail：38323490@qq.com引文格式：陈杰，罗喆，苏勇杰，等. 有机胺共沉淀法制备镍钴铝三元前驱体及表征［J］. 武汉工程大学学报，2019，41（5）：457-460.
更新日期/Last Update: 2019-10-29